Local mechanical and frictional properties of Ag/MoS2-doped selflubricating Ni-based laser claddings and resulting high temperature vacuum performance

Hector Torres, Harald Rojacz, Lucija Čoga, Mitjan Kalin, Manel Rodríguez Ripoll

Materials and Design 186 (2020) 108296.

Abstract

The present study investigates the local mechanical and frictional properties of Ag/MoS2-based self-lubricating claddings in order to unveil the contribution to friction reduction of the different phase constituents present in the cladding. The cladding microstructure is formed by nickel dendrites surrounded by borides and homogeneously scattered pure silver pockets encapsulated within molybdenum and chromium sulfides that arise from the thermal decomposition of MoS2 during deposition. Particular attention is devoted to the latter, since their local mechanical and frictional properties are completely unknown. The nanotribological results show that chromium sulfides have a high hardness and a low intrinsic friction. This implies a twofold role in friction reduction. They provide intrinsic low friction and support friction reduction by silver smearing thanks to their high hardness. The presented microstructure is able to effectively control and reduce friction down to a value of 0.25 in vacuum at room temperature and 300 °C by the smearing of silver over the chromium sulfides. This friction reduction mechanism is enhanced by thermal softening of the pure silver phase at elevated temperatures, contrary to air atmosphere, where smearing is hampered by silver oxidation. This overall tribological performance makes the presented claddings potential candidates for space applications.

 

URL: https://www.sciencedirect.com/science/article/pii/S0264127519307348

Keywords: Chromium sulphide, High temperature, Laser cladding, Self-lubrication, Vacuum tribology


Export bibliography